0086-510-81602872

Adhesive for MGO Panel

Adhesive for MGO Panel

Detail:

Adhesive For MGO Composite Sandwich Panel 
 
SPC-1003 Type two component polyurethane hand glue can be used for bonding granite tile with EPS, XPS, aluminum honeycomb, etc.
 
    
 
Application:
Adhesive for MGO board
Adhesive for magnesium oxide board
Adhesive for magnesium oxide sandwich panel 
Adhesive for MGO board to EPS core
Adhesive for MGO board to Expanded Polystyrene Foam
Adhesive for MGO sandwich panel 
Adhesive for MGO sheet
Adhesive for MGO wall panel
Adhesive for MGO panel
Adhesive for MGO wall board
Adhesive for MGO composite panel 
Adhesive for MGO board to MGO board
Adhesive for MGO board to steel sheet
Adhesive for MGO board to wood 
Adhesive for MGO board to XPS foam 
Adhesive for wall panel 
Adhesive for interior wall panel 
Adhesive for magnesium oxide board to eps core 
Adhesive for magnesium oxide board to Expanded Polystyrene Foam
Adhesive for magnesium oxide sandwich panel 
Adhesive for magnesium oxide sheet
Adhesive for magnesium oxide wall panel 
Adhesive for magnesium oxide panel 
Adhesive for magnesium oxide wall board 
Adhesive for magnesium oxide composite panel 
Adhesive for magnesium oxide board to magnesium oxide board 
Adhesive for magnesium oxide board to steel sheet 
Adhesive for magnesium oxide board to xps foam 


 
 
DESCRIPTION:

The two-component adhesive is widely used for bonding metal, wood, GFPR (glass fiber reinforced plastic), EPS/PU foam, rock wool, paper or aluminum honeycomb, etc. It is convenient in use, fast cured, high adhesion, superior in impact strength, tensile strength, weather resistance.


PRODUCT PROPERTIES:

Model SPC-1003
Component A Component B
Appearance Gray Uniform Emulsion Dark Brown Liquid
Viscosity(25℃) 12000-20000 Mpa.s ≥200 Mpa.s
Bonding Strength ≥10Mpa
Tensile Strength Metal and Metal≥10 Mpa(roomtemperature)                                          
Metal and Metal≥10 Mpa(low temperature)
Peel Strength Metal and nonmetallic material: nonmetallic material broken when peeled.
Shore Hardness 60-70
Solid Content 98%±2%
Applicable Time 50-80 Minutes(change according to temperature)
Time for Pressuring 5-8 Hours


APPLICATION INSTRUCTION:

1. Mixing component A and component B completely by motor stirrer. Mix ratio of A and B is 5:1~4:1 by weight.
2. Clean the target material surface. Ensure no water or putty on the surface.
3. Evenly spread the adhesive, about 150~300 g/mwith zigzag scraper of 5mm teeth space and 4mm teeth depth. Or spreading with roller. If making honeycomb sandwich panel, spreading more glue.
4. Cover the material with raising pressure for 60 minutes until the adhesive solidified.
5. Sealed store in a cool and dry place, avoid contact with water.
6. Storage temperature is 5℃~30℃. Shelf life is six months.
7. Package: Component A is 25kg/wide mouth plastic barrel; Component B is 25kg/small mouth plastic barrels.



PACKAGE: 25kg/plastic barrel
 




Contact

Ms Katrina

E-mail:info@puglue.com
Mob:0086 18915238982
Web:www.puglue.com

Copyright © 2014-2018 JIANGYIN SUNPING CHEMICAL CO., LTD. 
Address:Room 1101A, Huifeng Building, Jiangyin city, Jiangsu province, China

TEL:0086-510-81602872
 


wechat